Stainless steel characteristics and uses

Release Date:2016-10-18

Class character and use of ordinal number

1 austenite 1Cr17Mn6Ni5N nickel steel section, instead of grades 1Cr17Ni7, magnetic after cold working. Railway vehicles.

2.1Cr18Mn8Ni5N nickel steel section, instead of grades 1Cr18Ni9.

3.1Cr17Ni7 has a high intensity of cold processing. Railway vehicle, conveyor belt, bolt and nut.

4.1Cr18Ni9 has a high strength, but the elongation is slightly worse than that of 1Cr17Ni7. Decorative components for building.

5.Y1Cr18Ni9 enhances cutting and erosion resistance. The most suitable for automatic lathe. Bolt and nut.

6.Y1Cr18Ni9Se enhances cutting and erosion resistance. The most suitable for automatic lathe. Rivet, screw.

7.0Cr19Ni9 as the most widely used stainless steel, food equipment, general chemical equipment, atomic energy industry.

8.00Cr19Ni11 is lower than the 0Cr19Ni9 carbon steel, the resistance to intergranular corrosion is superior, for the welding does not heat treatment parts.

9.0Cr19Ni9N in the grade 0Cr19Ni9 plus N, the strength increases, the plastic does not reduce. Reduce the thickness of the material. Strength component for structure.

10.0Cr19Ni10NbN in the grade 0Cr19Ni9 plus N and Nb, with the same characteristics and uses of 0Cr19Ni9N.

stainless steel handrail

11.00Cr18Ni10N in the grade 00Cr19Ni11 plus N, with the same characteristics of the above grades, uses the same as the 0Cr19Ni9N, but the resistance to intergranular corrosion better.

Compared with 12.1Cr18Ni12 and 0Cr19Ni9, the work hardening property. Spinning processing, special drawing, steel.

13.0Cr23Ni13 corrosion resistance, heat resistance is better than 0Cr19Ni9.

14.0Cr25Ni20 is better than 0Cr23Ni13 in oxidation. Actually used as heat resistant steel.

15.0Cr17Ni12Mo2 in seawater and other kinds of media, corrosion resistance is better than 0Cr19Ni9. Corrosion resistant material.

16.0Cr18Ni12Mo2Ti for anti sulfuric acid, phosphoric acid, formic acid, acetic acid, have good resistance to intergranular corrosion.

Ultra low carbon steel 17.00Cr17Ni14Mo2 0Cr17Ni12Mo2, better than the 0Cr17Ni12Mo2 resistance to intergranular corrosion.

18..0Cr17Ni12Mo2N in the grade 0Cr17Ni12Mo2 to join N, improve the strength, does not reduce the plastic, so that the thickness of the material thinning. High strength components for corrosion resistance.

19..00Cr17Ni13Mo2N in the brand 00Cr17Ni14Mo2 to join the N, with the same characteristics of the above grades, uses the same as the 0Cr17Ni12Mo2, but better corrosion resistance.

20.0Cr18Ni12Mo2Cu2 corrosion resistance, corrosion resistance is better than 0Cr17Ni12Mo2. Sulfuric acid resistant material.

Ultra low carbon steel 21.00Cr18Ni14Mo2Cu2 0Cr18Ni12Mo2Cu2, better than the 0Cr18Ni12Mo2Cu2 resistance to intergranular corrosion

22.0C19Ni13Mo3 corrosion resistance is better than 0Cr17Ni12Mo2. For dyeing equipment, materials, etc..

Ultra low carbon steel 23..00Cr19Ni13Mo3 0Cr19Ni13Mo3, better than the 0Cr19Ni13Mo3 resistance to intergranular corrosion.

24.0Cr18Ni16Mo5 absorbs the heat exchanger, a chloride solution of acetic acid phosphoric acid bleaching equipment, equipment, installation, use in the application of the 00Cr17Ni14Mo2 and 00Cr17Ni13Mo3 environment.

25.1Cr18Ni9Ti as the core, instrumentation, medical equipment, diamagnetic acid containers and equipment lining pipeline equipment and spare parts etc..

26..0Cr18Ni11Ti add Ti to improve the resistance to intergranular corrosion, is not recommended for decorative parts.

27..0Cr18Ni11Nb containing Nb to improve intergranular corrosion resistance.

28 austenitic stainless steel 0Cr18Ni9.

Stainless steel with austenitic stainless steel at room temperature. The steel contains about 18% Cr, 8%~10% Ni, C about 0.1%, with a stable austenite structure. Austenitic chromium nickel stainless steel including the famous 18Cr-8Ni steel and on this basis to increase the content of Cr and Ni and join Mo, Cu, Si, Nb, Ti and other elements of the development of high Cr-Ni series steel. Austenitic stainless steel is not magnetic and has high toughness and plasticity, but the strength is low, it is not possible to strengthen through the phase transformation, only through the cold processing to strengthen. Such as the addition of Ca, S, Se, Te and other elements, it has a good machinability. This kind of steel in addition to the resistance to oxidation of acid corrosion, if it contains Mo, Cu and other elements can also be resistant to sulfuric acid, phosphoric acid, and formic acid, acetic acid, urea, etc.. If the carbon content in the steel is less than 0.03% or Ti and Ni, the corrosion resistance of the steel can be improved significantly. High silicon austenitic stainless steel concentrated nitric acid is willing to have a good corrosion resistance. As the austenitic stainless steel has comprehensive and good comprehensive performance, in all walks of life to obtain a wide range of applications.

29.0Cr18Ni13Si4

Adding Ni to the brand 9Ni9 0Crl, adding Si, increasing the stress corrosion cracking resistance. For more chlorine ion environment.

30 austenite - ferrite dual phase stainless steel 0Cr26Ni5Mo2

31.1Cr18Ni11Si4A1Ti

Parts and equipment for producing high temperature concentrated nitric acid medium

32.00Cr18Ni5Mo3Si2

Has a nose shape ferrite's dual phase microstructure, resistance to stress corrosion cracking performance, corrosion resistance and 00Crl7Nil3M02, with high strength for chlorine ion environment for industrial thermal refining, chemical fertilizer, papermaking, petroleum, chemical and other exchanger and condenser.

33 ferrite type

0Cr13A1

Cooling from high temperature does not produce significant hardening, steam turbine materials, quenching parts, composite steel

34.00Cr12

Low carbon content than 0Crl3, bending properties of the welding parts, processing performance, high temperature oxidation resistance. For automobile exhaust treatment device, boiler combustion chamber, nozzle

35 ferritic stainless steel 1Cr17

36.Y1Cr17